abrasion loss

基本解釋

Theory analysis and practice show (1) Define the parameter of power consumption and abrasion loss according the results of trial mill;
理論分析和實(shí)踐證明，要根據(jù)試驗(yàn)?zāi)サ膶?shí)驗(yàn)結(jié)果確定磨耗和功耗參數(shù)；
Results showed that the abrasion loss of EMP bearing increased with increasing of load and surface roughness of the pairs, but less than PTFE.
結(jié)果表明，油潤(rùn)滑時(shí)，含填充料彈性金屬型料軸承材料的磨損量隨負(fù)荷、對(duì)偶面表面原始粗糙度值增大而增加，但比純PTFE材料的磨損量低。
The results showed that the sample by adding the ultrafine powders of silica aerogel increased the tensile strength 54%, the elongation at break 64%, decreased the abrasion loss 20%.
試驗(yàn)結(jié)果表明，加入濕法白炭黑超細(xì)粉的試樣拉伸強(qiáng)度比添加氣相法白炭黑者提高了54％，扯斷伸長(zhǎng)率提高了64％，磨耗量降低了20％。