caustic embrittlement

基本解釋

With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.
隨著熱強(qiáng)堿腐蝕時(shí)間的延長(zhǎng)，高錳鋼的沖擊韌度明顯降低，堿脆開(kāi)裂是造成高錳鋼沖擊韌度下降的主要原因。
With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.
隨著鋼中含鉻量的增加，試驗(yàn)材料的活性溶解腐蝕失重增大，但堿脆開(kāi)裂的傾向減少。
The high Mn steel caustic embrittlement cracking was distinct in corrosion. With increasing corrosion time the impact toughness of high Mn steel obviously decreased.
隨著熱強(qiáng)堿腐蝕時(shí)間的延長(zhǎng)，高錳鋼的沖擊韌度明顯降低，堿脆開(kāi)裂是造成高錳鋼沖擊韌度下降的主要原因。