slag inclusion

基本解釋

B and the slag inclusion of slag inclusion dissolve after denoting to weld dregs the remnant phenomenon in weld.
夾渣夾渣是指焊后溶渣殘存在焊縫中的現(xiàn)象。
jacdulei.blog.163.com
The results showed that the oxidation slag inclusion and central porosity in the raw material were the direct reasons which the forging cracking.
結(jié)果表明，鍛坯原材料中存在的中心疏松和氧化物夾渣等低倍缺陷是導(dǎo)致鍛件開裂的主要原因。
This article analyzes the weld defects such as:blowhole, slag inclusion, incompletely filled groove, overlap, lack of fusion, undercut , over-sized leg, also it puts forward the solution.
對(duì)立角焊中氣孔、夾渣、未焊透、焊縫余高凸起、焊波脫節(jié)、咬邊、焊腳尺寸過(guò)大等缺陷產(chǎn)生的原因進(jìn)行了分析，并提出了有效的解決方法。