基本解釋[機] 回火馬氏體英漢例句雙語例句X-Ray analysis finds that steel after tempering main matrix of tempered martensite.用X-射線衍射分析發(fā)現(xiàn)，試驗鋼回火后的組織主要為回火馬氏體。The final structure obtained from tempering a fully hardened steel is called tempered martensite.回火完全淬硬鋼得到的最終組織結(jié)構(gòu)被稱為回火馬氏體。The strength of the steel was highest when aging at 470℃. The tempered martensite embrittlement appeared at 450℃ i. e. , the impact toughness was the lowesies.時抗拉強度達(dá)最高值，在450℃附近時效出現(xiàn)回火脆性，沖擊韌性處于低谷。tempered martensite更多例句詞組短語短語tempered -martensite embrittlement 回火馬氏體脆性tempered martensite embrittlement [機]回火馬氏體脆化acicular tempered martensite 針狀回火馬氏體tempered martensite structure 回韌麻田散組織over tempered martensite 過度回火馬氏體tempered martensite更多詞組專業(yè)釋義機械工程回火馬氏體回火索氏體土木建筑工程回火麻田散鐵